The Super Fast Leak Stopper!
Seal leaks in minutes, without heat.
METALCLAD SpeedAlloy QS begins to harden in just seconds. It is a 100% solids, high performance polymer composite that can be used to make effective repairs to all types of pipes, tanks and equipment which must be returned to service very quickly or where shut downs are not possible.
METALCLAD SpeedAlloy QS is a two-component system. The simple 1:1 mixing ratio insures easy mixing. It cures to super tough composite.
- Ultra Fast Curing
- Trowelable
- Requires No Heat
- Unlimited Shelf Life
- 100% Solids
- Safe & Simple To Use
Use on...
- Pipes & Tanks
- Sumps
- Radiators & Fuel tanks
- Cracked & holed casings
- Seams
Technical Data
- Volume capacity per 250gm unit
- 10.5 in3 / 172 cc
- Mixed density
- 0.085 lbs per in3 / 2.33 gm per cc
- Coverage rate per 250gm unit @ 0.25 in / 6mm
- 42 in2 / 0.027 m2
- Shelf life
- Indefinite
- Volume Solids
- 100%
| Mixing ratio | Base | Activator |
|---|---|---|
| By Volume | 1 | 1 |
| By Weight | 1 | 1 |
Working Life and Cure Times
| Ambient Temperature | Working Life | Light Load | Full Mechanical | |
|---|---|---|---|---|
| 41°F | 5°C | 5 min. | 30 min. | 2 hrs. |
| 59°F | 15°C | 2 min. | 10 min. | 1 hrs. |
| 77°F | 25°C | 1 min. | 5 min. | 40 min. |
| 86°F | 30°C | 45 sec. | 3 min. | 30 min. |
Physical Properties
| Typical Values | Test Method | ||
|---|---|---|---|
| Compressive strength | 11,000 psi | 770 kg/cm2 | ASTM D-695 |
| Hardness - Shore D | 80 | ASTM D-2240 | |
| Tensile Shear Adhesion | |||
| Steel | 2100 psi | 147 kg/cm2 | ASTM D-1002 |
| Aluminum | 1900 psi | 133 kg/cm2 | ASTM D-1002 |
| Copper | 1800 psi | 126 kg/cm2 | ASTM D-1002 |
| Stainless Steel | 2000 psi | 140 kg/cm2 | ASTM D-1002 |
SpeedAlloy QS has an extremely fast initial set time, making it the ideal material for stopping the flow and effectively plugging active leaks. The use of SpeedAlloy QS, allows time for proper surface preparation and application of either standard SpeedAlloy or DurAlloy (over the SpeedAlloy QS) for a long-term repair.